Abstract
We prepared the nanocrystals (NCs) of CdTe, CdTe:Yb, and CdTe:Yb, Mn vis water phase synthesis and examined their structural, morphological, and optical properties. All NCs have a particle diameter of about 2–4 nm, and the monodispersed, uniform spherical, cubic structure of the CdTe NC remains largely unchanged after the doping with Yb and Mn. According to the X-ray diffraction results, the CdTe, CdTe:Yb, and CdTe:Yb, Mn NCs all have a cubic structure, and the diffraction peak of CdTe:Yb NC is at a lower 2θ angle compared with that of the CdTe NC. With the CdTe NC as the reference, the UV–Vis absorption of the CdTe:Yb and the CdTe:Yb, Mn NCs exhibits a blueshift and a redshift, and the emission of CdTe:Yb and CdTe:Yb, Mn has a blueshift of about 12 nm and a redshift of about 73 nm, respectively. The CdTe:Yb, Mn NCs have higher quantum yields than the CdTe:Yb NC, and the quantum yield is the highest when CdTe is doped with 1:1 Mn2+/Yb3+. In addition, both the CdTe:Yb and CdTe:Yb, Mn NCs have a shorter fluorescence lifetime than the CdTe NC.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.