Abstract
Single crystals of Yb:RbTiOPO(4) codoped with Nb(5+) or Ta(5+) were grown by the top seeded solution growth slow-cooling technique. The ytterbium concentration in the crystals varies as a function of the molar ratio of the precursor oxides and of the codopant, reaching a maximum value of 1.9x10(20) Yb(3+) ions/cm(3). The broad band near 1 mum in absorption and emission spectra at room temperature is due to the large splitting of the Yb(3+) ground state. The ytterbium (2)F(5/2) level radiative lifetime in Nb:RbTiOPO(4) (tau(rad) = 2.7 ms), was calculated and then compared to the measured fluorescence decay time (tau(em) = 2.2 ms), giving an intrinsic quantum efficiency of 81%. To evaluate the potentiality of these crystals for self-frequency doubling, preliminary results of Yb(3+) laser operation and fundamental wavelength measurements for type-II non-critical second harmonic generation ( lambda(NCPM)) are also reported.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.