Abstract
High brightness Y3Al5O12:Tb phosphor particles with spherical shape and fine size were prepared by spray pyrolysis from spray solution with polymeric precursors and ammonium fluoride flux. The effect of ammonium fluoride flux on the characteristics of the Y3Al5O12:Tb phosphor particles prepared by spray pyrolysis was investigated. Ammonium fluoride flux dissolved into spray solution improved the photoluminescence intensity of the Y3Al5O12:Tb phosphor particles prepared by spray pyrolysis. The optimum addition amount of ammonium fluoride flux to produce the maximum photoluminescence intensity was 1 wt.% of the Y3Al5O12:Tb phosphor particles. The spherical shape of the as-prepared particles obtained by spray pyrolysis from spray solution with polymeric precursors and small amount of ammonium fluoride flux had maintained after post-treatment below 1300 °C. The optimum photoluminescence intensity of the Y3Al5O12:Tb phosphor particles prepared from polymeric precursors and ammonium fluoride flux was 156% of that of the phosphor particles prepared from pure aqueous solution.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.