(Y3+/Sm3+)-doped and co-doped CoFe2O4 for heterogeneous advanced oxidation process: structural, magneto-optical, and photocatalytic investigations.

Abstract

The photocatalytic properties of CoFe2O4 nanoparticles were activated by the doping and co-doping of a low level of Y3+ and Sm3+ cations. After optimizing the annealing temperature, 900°C was found to be the optimal temperature for the successful incorporation of Y3+ and Sm3+ into the spinel structure. The purity of our samples annealed at 900°C was confirmed using several characterization methods, including PXRD, SEM, XPS, VSM, FTIR, and Raman spectroscopy. Thus, we were able to increase the photocatalytic degradation of orange G dye from 9.9 to 64.63% for the Sm3+-doped sample, 76.42% for the Y3+-doped sample, and even 85.81% for the co-doped sample under 60min of UV-visible light irradiation. The beneficial effect of samarium and yttrium doping and co-doping is attributed to several factors: the first factor is doped and co-doped rare earth impurities induce distortion in the lattice, the larger the ionic radii of dopant element, the highest is the photocatalytic activity; second factor, upon doping and co-doping of rare earth impurities in the structure of CoFe2O4 leads to the creation of donor state level within the band gap, causing the Fermi energy to shift near the conduction band. Third factor, co-doping produced strong interactions, which accelerated photocarrier mobility and transport; lastly, longer electron-holes lifetime. We have provided a detailed study of the structural, vibrational, and optical properties to support our conclusions.