Y, Yb, and Gd tri-doping on B-site of Ba(Zr, Ce)O3-δ with improved proton conduction performance

Abstract

Perovskite-type proton conducting electrolytes are garnering significant attention due to its key role in protonic ceramic electrochemical cells (PCEC) and its application in hydrogen sensors (HS) used for metal melt measurements. Developing high proton conduction perovskite materials with good chemical stability is always a worldwide research focus. In this paper, Y, Yb and Gd triple-doping on B-site of BaCeO3-BaZrO3 solid solution were carried out to investigate the effect of gadolinium doping on the performance of protonic conducting electrolytes. BaZr0.1Ce0.7(Y0.5Yb0.5)0.2-xGdxO3-δ (x = 0, 0.1, 0.15 and 0.2), which were also referred as BZCYYbGdx (x = 0, 10, 15 and 20), were synthesized by solid-state reaction at 1600 °C for 10 h. It is found that BZCYYbGd15 has the highest proton conductivity and proton transfer number among the four prepared materials. The proton mobility of BZCYYbGd15 is 4.06 × 10−6 cm2/(Vꞏs) at 800 °C, which increases with an increased temperature. Its proton transfer number is higher than 0.9 at 500 °C under the atmosphere of PH2O = 0.018 atm. A moderate doping of gadolinium increases the temperature threshold for proton conduction. Proton, oxygen vacancy, electron hole and total conductivity activation energies of BZCYYbGd15 under the wet atmosphere are found to be 0.74, 1.58, 1.41 and 0.92 eV, respectively. Furthermore, the chemical stability of pellets is improved after gadolinium doping. This study provides a reference value for future research on high proton conduction electrolytes.