Abstract
Overlapping tracks were produced by laser processing using a powder SiC (∼6 μm) preplacement technique which has been developed to modify the surface structure of a Ti–6Al–4V alloy. A continuous-wave CO 2 laser was used for the processing which produced six overlapping tracks covering 14 mm across the surface of a 10 mm thick plate. Under spinning beam conditions, a surface alloyed/metal matrix composite (MMC) layer over 300 μm in depth was produced on the alloy. The surface contained a complex microstructure, but with no cracks and only two pores at the melt/HAZ interface. Using XRD and XPS analysis, it was shown that the solidified melt consisted of α′-Ti, Ti 0.55C 0.45 and Ti 5Si 3 phases, which vary with melt depth and with the particular group of overlapping tracks examined. Therefore, no new phases to those previously identified in single track laser processing experiments were found in this work.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.