Abstract
AbstractWood is thermally modified by heating and steaming in order to change its properties, e.g., to improve the biological resistance and to increase the hardness of wood. The structure of thermally modified Scots pine (Pinus sylvestris) was studied using wide-angle, small-angle and ultra-small-angle X-ray scattering methods. Modification temperatures varied from 100 to 240°C. No marked changes in the microfibril angle distribution were observed. The mass fraction of crystalline cellulose in wood (the crystallinity of wood) and the size of cellulose crystallites increased above 150°C. After modification at 230°C for 4 h the thickness of the cellulose crystallites increased from 3.1 to 3.4 nm. Thermal modification had no effect on the orientation of the voids, but an increase in the porosity of the cell wall was observed. The distance between cellulose crystallites was approximately 4.7 nm in hydrated wood and a decrease in order between microfibrils was observed at 160–200°C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.