Abstract
X-ray and neutron diffraction studies were carried out on highly ordered (2−3% Li/Ni exchange) layered Li1-xCo1/3Ni1/3Mn1/3O2 [(1 − x) = 1.0; 0.8, 0.6, 0.45, 0.30, 0.04] prepared by chemical delithiation and relithiation. The studies reveal that the initial R3̄m phase (O3) is maintained up to extraction of 0.70−0.75 Li and exhibits only ∼1% change in volume over the range of composition. Additional extraction of Li results in the appearance of the O1 phase (trigonal; P3̄m1), which displays a strong contraction in the c axis by 5.3% and a volume decrease of 7.2%. Oxygen vacancies were not evident in the completely delithiated material. Re-intercalation of lithium in this phase was relatively irreversible, however, resulting in poorly defined mixtures of the O3 and O1 structures that exhibited a large fraction of stacking faults. In contrast, materials that were not delithiated beyond x = 0.30 resulted in fully reversible reformation of the original crystalline O3 phase on re-intercalation. Electrochemical cycling under different cutoff voltages were in accord with these observations and suggest an optimum upper cutoff voltage of 4.3−4.4 V.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.