Abstract
AbstractSuperconducting thin films (0.3-0.7μm) in the TI-Ca-Ba-Cu-0 system have been prepared on various single crystal substrates by sequential electron beam evaporation followed by appropriate sintering and annealing. Oxygen-annealed films show Tc as high as 110K and critical current densities to 600,000 A/cm2. X-ray diffraction analyses of these films show predominantly the Tl2Ca2Ba2Cu2O10 phase (c-parameter near 36Å), but some also contain up to 50 at% of the Tl2CaBa2Cu2O8 phase (c-parameter near 30Å). The complete absence of hkl reflections other than 00I demonstrates the highly oriented nature of the films as well as the absence of other Tl phases. The diffraction peaks are noticeably broader for the 36Å phase than for the 30Å phase. For a 0.7μm film such broadening is consistent with coherent sizes along the c-axis of 1200 - 1400Å and 500Å, respectively, for the 30Å and 36Å phases, and of strain values near 1.4-1.8 x 10-3 for both phases.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.