Abstract
Structural modifications of Al thin films implanted with Mn + ions at liquid-nitrogen-temperature (LNT) (∼77 K) were studied by X-ray powder diffraction. For each Mn concentration, strain and crystallite size were determined from X-ray line broadening. For room-temperature (RT) implantation, amorphization begins at approximately 1 at.% Mn by thermally activated local atomic rearrangements which lead to the formation of amorphous zones or clusters. At LNT, a supersaturated solid solution is formed at mean Mn concentrations below 5 at.% Mn. At higher Mn concentrations, amorphous clusters formed throughout the sample in regions where the strain level reached a threshold value at a critical Mn concentration of 8.5%. Present investigations suggest a preferential short-range migration of Mn atoms from the remaining crystalline material to amorphous regions formed at LNT causing an Mn depletion and partial recovery of the crystalline regions. The maximum value of the atomic displacements U st was found to be 0.13 ± 0.01 Å and the maximum value of the strain was (1.65 ± 0.15) × 10 −3. The lattice constant a 0 of the host (Al) lattice was found to decrease by about 0.13%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.