Abstract
Abstract In this work, the process of formation of metastable phases was investigated for the Fe75B25 composition. Mechanical synthesis was performed in a MAPF-2M high-energy planetary ball mill under an argon atmosphere. X-ray diffraction (XRD), differential scanning calorimetry (DSC), and Mössbauer spectroscopy (MS) were applied to recognize the phases. After 6 h of milling, the material consisted of two phases, that is, metastable tetragonal t-Fe2B and amorphous phases. During further thermal processing, the metastable phase was transformed into the stable Fe2B phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.