Abstract
This article shows a study of the effect of mechanical activation of the initial mixture of reagents NiO and Fe2O3 at different speeds of grinding bowl rotation on synthesis of nickel ferrite. Nickel ferrite was produced by the solid-phase synthesis at a temperature of 900 °C for 240 minutes. The obtained ferrite samples were investigated by thermal gravimetric and X-ray phase analysis. The Curie temperature values are obtained, as well as the magnitude of the change of detected instrument weight at the magnetic phase transition (ferromagnetic-paramagnetic) of nickel ferrite using thermal gravimetric curves (TG/DTG) with applied external magnetic field. Increasing of the homogeneity degree of ferrite materials with an increase in the mechanical activation rate is shown based on the data of X-ray phase analysis. The experimental results obtained from thermal, magnetic, and X-ray analyzes were compared.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.