Abstract
Indium tin oxide (ITO) films (physical thickness, 250–560±25nm) were deposited on soda lime silica (SLS) glass and silica layer coated (∼200nm physical thickness) SLS glass substrates by sol–gel technique using alcohol based precursors containing different In:Sn atomic percentages, namely, 90:10, 70:30, 50:50, 30:70. Cubic phase of In2O3 was observed up to 50at.% Sn while cassiterite SnO2 phase was observed for 70at.% Sn. Work function of the films was evaluated from inelastic secondary electron cutoff of ultraviolet photoelectron spectroscopy (UPS) energy distribution curve (EDC) obtained under two experimental conditions (i) as-introduced (ii) after the cleaning of the surface by sputtering. Elemental distribution and the presence of oxygen containing contaminant and carbon contaminant of the samples were done by XPS analysis under same conditions. The work function changed little due to the presence of surface contaminants. It was in the range, 3.9–4.2eV (±0.1eV).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.