Abstract
The effects of outside and accelerated (xenon-arc and UVA) weathering on the visual appearance and chemical changes of wood plastic composite (WPC) formulations based on high density polyethylene (HDPE) and polypropylene (PP) were investigated. Colorimetry, scanning electron microscopy, Fourier transform infrared spectroscopy (FT-IR), and pyrolysis–gas chromatography–mass spectrometry (Py–GC–MS) were employed in this study. The study showed that for both outside and accelerated weathering, longer exposure time increased the degree of color change (and lightness), carbonyl concentrations, and wood loss on weathered WPC surfaces. HDPE-based WPC exhibited decreased lightening, carbonyl concentrations, and wood content loss when compared to PP-based WPC. From this study, relationships between chemical and color changes that occurred during exterior weathering of HDPE-based WPC were established. Oxidation and degradation of wood lignin influenced WPC color changes (lightening) during weathering.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.