Abstract
We prepared PTA coating solution by hot plate evaporation, N2 bubbling evaporation, and rotary evaporation. N2 bubbling and rotary evaporation are very efficient way to synthesize PTA which reduces the synthesis process time to 1/5, compared to hot plate evaporation method. Another strong point is that N2 bubbling and rotary evaporation make it possible to control excess hydrogen peroxide and water contents in PTA. The PTA formula were WO3·0.13H2O2·10.0H2O for hot plate method, WO3·0.16H2O2·7.1H2O for N2 bubbling method, and WO3·0.15H2O2·3.00H2O for rotary evaporation method. Thermal analysis and mass spectroscopy analysis show that water is evaporated at around 100 °C and hydrogen peroxide is dissociated at the range of 150 and 250 °C. Amorphous phase of WO3 thin film prepared from rotary evaporated PTA solution has the best electrochromic property, light transmission difference from 91% at its bleached state and 5.5% colored state, and charge density of 22 mC/cm2. It is thought that the control of excess hydrogen peroxide and water contents in PTA is very important to enhance the electrochromic properties of WO3 thin film.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.