Abstract

AbstractPolyethylene glycol (PEG), polypropylene glycol (PPG), and poly(ethylene glycol‐co‐propylene glycol) (PEPG) of number average molar masses (Mn) of 6–20 kDa are used as macroinitiators in the ring‐opening polymerization (ROP) of l‐lactide to synthesize high molar mass (50 kDa < MnCopo < 120 kDa) PLLA‐b‐polyether‐b‐PLLA linear triblock and starblock copolymers. At the studied block lengths, PEG and PEPG blocks exhibit miscibility with the PLLA blocks in the amorphous domains leading to a plasticization effect. As the PEG or PEPG block content is increased to 18 %wt, the Tg (Tg ≈ 24 °C) and the elastic modulus (E ≈ 500 MPa) are reduced, while the elongation at break (εb ≈ 280%) and crystallization rate are increased. At the same time, small angle oscillatory shear (SAOS) rheometric measurements show that the plasticized copolymers have a reduced melt viscosity. In contrast, SAOS and DSC measurements of the PPG‐containing block copolymers reveal phase separation of the PPG and PLA blocks leading to microstructures in the melt. Tensile tests show that the phase‐separated PPG‐containing block copolymers are more ductile than PLA homopolymers, but more brittle than the PEG‐ or PEPG‐plasticized block copolymers.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.