Abstract
In this study, α-Fe2O3 nanowires were synthesized using mesoporous SBA-15 silica as the hard templates with the nanocasting method, and then mesoporous α-Fe2O3 nanowire bundles (NWBs) were separated from the well-dispersed α-Fe2O3 nanowires (NWs) by the centrifugation technique. Both samples were characterized by x-ray diffraction, transmission electron microscopy (TEM), nitrogen adsorption/desorption isotherm and UV-vis spectra. All results indicated that the α-Fe2O3 NWBs with mesoporous structure presented a higher BET surface area (95 m2 g−1) and wider bandgap (2.08 eV) than those of α-Fe2O3 NWs (32 m2 g−1 and 1.91 eV). The bandgap of α-Fe2O3 NWBs was in accordance with the bulk α-Fe2O3, while the BET surface area was much higher. The results from the gas-sensing measurement revealed that the α-Fe2O3 NWBs based gas sensor exhibited a high sensitivity of 21.7, fast response-recovery of 7.5 s and 1 s, and good selectivity to ethanol at 340 °C. The sensitivity (21.7) for ethanol of α-Fe2O3 NWBs was much better than that of the α-Fe2O3 NWs (12.2), which should be attributed to the higher BET surface area and wider bandgap of α-Fe2O3 NWBs.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.