Abstract
Whisker behavior at various surface treatment conditions of pure Sn plating are presented. The temperature cycling test for 600 cycles and the ambient storage for 1 year was performed, respectively. From the temperature cycling test, bent-shaped whiskers were observed on matte and semibright Sn plating, and flower-shaped whisker on bright Sn plating. The bright Sn plating has smaller whiskers than the other types of Sn plating, and the whisker growth density per unit area is also lower than the others. After 1 year under ambient storage, nodule growth of FeNi42 lead frame (LF) was observed in some parts. The Cu LF showed about a 9.0 µm hillock-shaped whisker. This result demonstrated that the main determinant of whisker growth was the number of temperature cycling (TC) in the FeNi42 LF, whereas it was the time and temperature in the Cu LF. Also, whisker growth and shape varied with the type of surface treatment and grain size of plating.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.