Abstract
AbstractWe report the synthesis and thermosensitive properties of well‐defined water‐soluble polyacrylates and polystyrenics with short pendant oligo(ethylene glycol) groups. Four monomers, methoxydi(ethylene glycol) acrylate (DEGMA), methoxytri(ethylene glycol) acrylate (TEGMA), α‐hydro‐ω‐(4‐vinylbenzyl)tris(oxyethylene) (HTEGSt), and α‐hydro‐ω‐(4‐vinylbenzyl)tetrakis(oxyethylene) (HTrEGSt), were prepared and polymerized by nitroxide‐mediated radical polymerization with 2,2,5‐trimethyl‐3‐(1‐phenylethoxy)‐4‐phenyl‐3‐azahexane as an initiator. Kinetics and gel permeation chromatography analysis showed that the polymerizations were controlled processes yielding polymers with controlled molecular weights and narrow polydispersities. All polymers could be dissolved in water, forming transparent solutions, and undergo phase transitions when the temperature was above a critical point. The thermosensitive properties were studied by turbidimetry and variable‐temperature 1H NMR spectroscopy. The cloud points of the polymers of DEGMA, TEGMA, HTEGSt, and HTrEGSt were around 38, 58, 13, and 64 °C, respectively. For all four polymers, the cloud point increased with decreasing concentration and increasing molecular weight in the studied molecular weight range of 5000–30,000 g/mol. The removal of the nitroxide group from the polymer chain end resulted in a higher cloud point. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2454–2467, 2006
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Polymer Science Part A: Polymer Chemistry
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.