Abstract
The welding solidification cracking susceptibility of ERNiMo-2 wire was studied by trans-varestraint test. Results show that the threshold strain and saturated strain are 4% and 8% respectively. In this range, the maximum crack length increases continuously with strain. Solidification cracks occur in interdendrites and extend along solidification grain boundaries. The strain and eutectic M6C which reducing the binding force of grain boundaries, are the main factors affecting the solidification cracking. The segregation of Si and P at the grain boundary is also beneficial to the formation of liquid film, which enlarges the solidification temperature range and further increases the welding solidification cracking susceptibility of weld metal.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.