Abstract
To expand the application of laser-MIG hybrid welding in the arc-welded aluminum alloy profile manufacturing for high-speed trains, the laser-MIG hybrid welding characteristics of 4 mm thick A6N01S-T5 arc-welded aluminum profiles were studied in this work. The welding parameters were optimized using the orthogonal test; the microstructure and properties of the joints were analyzed. The results showed that the optimal welding parameters were: welding speed 1.0 m/min, laser power 2.7 kW, arc current 200 A, spot diameter 0.8 mm, heat source distance 3 mm, and defocusing amount 0 mm. The columnar crystals and dense dendrites were observed near the fusion line and in the weld center, respectively, and the grains in the heat-affected zone were slightly coarse. The microhardness of the softening zone in the heat-affected zone was the lowest. The average tensile strength of the joints was 212 MPa, about 86% of the base metal. The samples fractured in the heat-affected zone, and the fractures showed typical plastic fracture characteristics. The results showed that laser-MIG hybrid welding has good applicability and feasibility for the arc-welded profile welding manufacturing.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.