Abstract

Welding is a commonly used and one of the most important material-joining processes in industry. The incidences of defects had been located by ultrasonic testing (UT) in various pressurizer nozzle dissimilar metal welds (DMW) at nuclear power plants. In order to evaluate the crack propagation, it is required to calculate the stress distribution including weld residual stress and operational stress through the wall thickness in the weld region. The analysis procedure in this paper included not only the pass-by-pass welding steps, but also other essential fabrication steps of surge, safety/relief and spray nozzles. In this paper, detailed welding simulation analyses have been conducted to predict the magnitude of these stresses in the weld material. To prevent primary water stress corrosion cracking (PWSCC) in pressurized water reactors (PWR) on susceptible welded pipes with dissimilar metal welds, the weld overlay process has been applied to repair nuclear reactor pipe joints in plants. The objectives of such repairs are to induce compressive axial residual stresses on the pipe inside surface, as well as increase the pipe thickness with a weld material that is not susceptible to stress-corrosion cracking. Hence, understanding the residual stress distribution is important to evaluate the reliability of pipe joints with weld overlay repairs. The finite element results in this paper showed that, after deposition of the DMW nozzle and stainless steel welds, tensile weld residual stresses still exist at regions of the DMW through the thickness. This tensile weld residual stress region was significantly reduced after welding the overlay. The overlay weld also provides a more uniform and large compressive region through the thickness which has a beneficial effect on the structural integrity of the DMW nozzle welds in the plant.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call