Abstract
Tensile and wear properties of aluminium (Al) based metal matrix composites (MMCs) was prepared by added titanium diboride (TiB2) with in-situ technique by salt route. The salts used in this research were potassium hexafluorotitanate (K2TiF6) and potassium tetrafluoroborate (KBF4). Nanocomposite samples were prepared by casting technique associated with incorporating 3 and 6 wt.% of TiB2 into matrix of Al-6wt.%Cu. Instron and wear tests machine were used to characterize the tensile and wear Al-Cu alloys properties. Results showed that increase in TiB2 content gave the high properties of tensile and wear behavior. The study indicates that TiB2 particles have giving improvement the wear performance of the Al–6wt.%Cu alloy. For a constant load and sliding speed, the wear rate decreases as a function of amount of TiB2 in the composite. The wear rate decrease with increasing in wt.% TiB2 particles for the all loads applied. However, addition of TiB2 particle to the Al–6 wt%.Cu matrix has show the coefficient value of wear decreases regardless of applied load. Study of the wear surfaces both alloy and composites by optical microscope suggests that the improvement in wear resistance is mainly due to the formation of finer groove or debris by content of TiB2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.