Abstract
Thin hard physical vapor deposited (PVD) coatings play significant role on wear performance of fine-blanking punches in the presence of extremely high contact stresses. Nevertheless it seems that in blanking or fine-blanking the coatings are selected based on coincidence, trial-error-method or latest trends. There is limited information about planning and conducting the fine-blanking industrial field tests and measuring the wear of different coatings. In the present study a set of fine-blanking punches and laboratory specimens were prepared with three coatings – TiCN, nACRo and nACo. As substrate material Bohler S390 Microclean high speed steel was used. Coating mechanical properties (modulus of elasticity and nanohardness) were measured and wear rate with alumina ball was determined using the reciprocating sliding test. Wear of coatings was measured from punches after industrial use. All of the tested coatings showed high variance of wear. However coatings nACo and nACRo have better average wear resistance in fine-blanking compared with the well-known TiCN. Industrial field tests show correlation to the ratio elastic strain to failure H/E. DOI: http://dx.doi.org/10.5755/j01.ms.21.3.7249
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.