Wear behaviors of HVOF sprayed WC-12Co coatings by laser remelting under lubricated condition

Abstract

A HVOF (high velocity oxygen fuel) sprayed WC-12Co coating was remelted with a CO2 laser. The surface-interface morphologies and phases were analyzed by means of SEM (scanning electron microscopy), and XRD (X-ray diffraction), respectively. The friction and wear behaviors of WC-12Co coating under the dry and lubricated conditions were investigated with a wear test. The morphologies and distributions of chemical elements on worn scar were analyzed with a SEM, and its configured EDS (energy diffusive spectrometer), respectively, and the effects of lubricated condition on COFs (coefficient of friction) and wear performance were also discussed. The results show that the adhesion between the coating and the substrate is stronger after laser remetling (LR), in which mechanical bonding, accompanying with metallurgical bonding, was found. At the load of 80N, the average COF under the dry and lubricated friction conditions is 0.069, and 0.052, respectively, the latter lowers by 23.3% than the former, and the wear rate under the lubricated condition decreases by 302.3% than that under the dry condition. The wear mechanism under the dry and lubrication conditions is primarily composed of abrasive wear, cracking, and fatigue failure.