Abstract
A Ni-WC coating was fabricated successively on a copper substrate by laser. The microstructure, hardness and wear resistance were investigated. The thickness of Ni-WC coating was 0.65mm and average hardness of strengthening layer was 667HV0.1, which was approximately 7.8 times higher than the hardness of copper substrate. The wear volume of Ni-WC coating was only 0.014mm3, which was only 1.02% wear volume of copper substrate. The decrease in wear volume was mainly due to presence of reinforced phases, such as γ-Ni, Cr0.19Fe0.7Ni0.11, M7C3, M23C6 and WC. In addition, there was no coating peeled off after 100 times trials of heat shock resistance experiment at 800℃. The experimental results show that this Ni-WC coating has a good metallurgical bonding strength and hardness, and it also has good wear resistance and high temperature property, which is helpful to improve the service life of mould copper plate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.