Abstract
420/WC-17Co coating was deposited on AZ80 magnesium alloy substrate by cold spraying technology. SEM was used to characterize the original powder morphology and coating microstructure. The microhardness and bonding strength of as-sprayed coating were tested by microhardness tester and universal material testing machine. Moreover, friction and wear property of the coating was also investigated by a ball-on-disk tribometer. Corrosion behaviours of coatings and magnesium alloy were characterized by electrochemical measurements. The results show that high quality 420/WC-17Co coating can be deposited on AZ80 magnesium alloy by cold spraying technology. The microhardness of cold sprayed 420/WC-17Co coating is (615 ± 62) HV, bonding strength is (57 ± 11) MPa and wear rate is only 3.3 × 10–6 mm3·N·m. The wear resistance of cold sprayed 420/WC-17Co coating is improved by two orders of magnitude, and the corrosion current density is reduced by one order of magnitude than magnesium alloy substrate. In conclusion, the present research demonstrates that cold sprayed 420/WC-17Co coating can significantly improve the surface performance of magnesium alloy substrate without evident heating output.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.