Abstract
The effect of thermal treatment on the wear and corrosion behavior of three categories of Cu-Zn-Sn-Fe SMAs designated A, B, and C is studied. Wear properties were investigated using a tribometer whilst corrosion in 0.3 M H2SO4and 3.5%NaCl media was studied using the potentiodynamic polarization method. The microstructure of the alloys mainly consists of FCC Cu-rich phase and Cu5Zn8phase. The up-quenched A alloys show the highest hardness and lowest wear rate values of 72.1 HRB and 0.143 mm3/N/m respectively. Average COF was higher for the samples subjected to direct-quenching (0.35–0.12) than the up-quenched (0.16–0.12) and step-quenched (0.2–0.08) samples. Wear occurred by mixed mode mechanisms of abrasion and adhesion evident by grooves and wear particles on the surface. In 0.3 M H2SO4medium, step-quenched alloys had corrosion rates in the range of 0.1022 to 1.1705 mm/yr, which is lower than the range of 0.1466 to 0.2855 mm/yr, and 0.1730 to 0.6027 mm/yr obtained for direct quenched and up-quenched samples respectively. In 3.5% NaCl solution, step-quenched alloys had the lowest corrosion rates 0.0251 mm/yr relative to samples subjected to up-quenching and direct quenching treatment. Generally, step-quenching treatment effectively improved the corrosion resistance of alloys in both media.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.