Abstract
The performance of zirconia toughened alumina with addition of MgO additives is investigated. Optimized composition of MgO at 1.1 wt% was used in the composition with alumina/yittria stabilized zirconia (YSZ). The composition was mixed, uniaxially pressed into rhombic 80o cutting inserts with 0.8 mm nose radius and sintered at 1600oC for 4 h in pressureless condition. For machining analysis, commercial stainless steel 316L with 12 mm diameter were used as workpiece. The workpiece was machined at 625 to 1750 rpm. Tool wear and surface roughness of workpiece were measured. Result shows three types of wear behaviour appear which are flank wear, notch wear and chipping. Flank wear and notch wear increased with the cutting speed but decrease by increasing the feedrate before increased after passing the 0.2mm/rev feedrate. While chipping very much related to the feedrate as the chipping area increased when the feedrate increased. Meanwhile, surface roughness increase with increment of cutting speed and feedrate which match the wear pattern.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.