Abstract
AbstractGadolinium oxide films, prepared by the sol–gel process, present waveguiding properties. Their structures were studied by waveguide Raman spectroscopy (WRS) and confirmed using transmission electron microscopy (TEM). The structural evolution of the layers with annealing temperatures from 650 up to 900°C was investigated. The WRS results and TEM observations were correlated and revealed that crystallization started at 650°C into the cubic phase. The mean diameter of the crystallites dispersed in the amorphous phase is around 5 nm at this temperature. The film is totally crystallized into the cubic phase at 700°C. The monoclinic phase simultaneously appears at 800°C and both phases still co‐exist after heat treatment at 900°C. The films present a heterogeneous structure at 900°C with grain sizes varying from 5 up to 50 nm and as consequence their waveguiding properties strongly decrease. Copyright © 2003 John Wiley & Sons, Ltd.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.