Abstract
High lithium ion conductivity solid electrolytes of Li1.4FexAl0.4 - xTi1.6(PO4)3 (x = 0−0.4) with the NASICON-type structure were synthesized by using a sol−gel precursor. The highest electrical conductivity was obtained for Li1.4Fe0.25Al0.15Ti1.6(PO4)3 sintered at 1040 °C for 7 h in air. The total, grain boundary, and bulk conductivities of the pellet were 1.01 × 10-3, 2.17 × 10-3 and 1.81 × 10-3 S cm-1 at 25 °C, respectively. The contribution of electron (or hole) conductivity to the total conductivity was negligibly small. Li1.4Fe0.25Al0.15Ti1.6(PO4)3 was unstable in water, but stable in saturated LiOH and LiCl aqueous solutions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.