Abstract
The water corrosion of tungsten as a target material can affect the safe operation of accelerator-driven neutron source. This paper reported the corrosion behaviors of tungsten in ultrapure water and tap water for 7, 14, 21, 30 and 60 days. Moreover, ICP-MS, XRD, XPS, SEM-EDS and LSCM were used to analyze the components in solutions, crystalline structures, chemical compositions and surface morphologies. It was found that the dissolution of tungsten, due to corrosion, reached its maximum between 30 days and 60 days in both solutions. The cube-shape substance, CaWO4, was the main corrosion product after tungsten in tap water. The tungsten oxide was changed from WO3 to WO2 during the corrosion of tungsten in ultrapure water. Compared with tungsten in ultrapure water, tungsten in tap water had its surface completely destroyed, with a dense diamond shape. Therefore, based on the analysis from this study, the corrosion mechanisms of tungsten in ultrapure and tap water were revealed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.