Abstract
Poly(acrylic acid) (PAA) is added as a binder to the water-based slurry of Ni-rich Li(Ni0.8Co0.1Mn0.1)O2 (NCM811) powder. After adding PAA, the pH of the slurry changes from strongly alkaline to nearly neutral (pH9.0), making it suitable for casting on the aluminum current collector without corroding the aluminum (Al) and a largely increased adhesion from 318 to 458 kg m−2 after drying. The use of PAA also improves the dispersion of the slurry, because the carboxyl groups of PAA can interact with NCM811 to help stabilize the electrode particles in the slurry. Given the improved dispersion, reduced corrosion potential, and better adhesion, the resultant NCM811 cathode exhibits good structural integrity and greatly lowered charge-transfer resistance from 37.0 to 8.5 Ω, showing a high initial capacity of 189.2 mAh g−1 and capacity retention of 84.2% after 100 charge-discharge cycles under 0.2C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.