Abstract
The warm stretch formability and flangeability of 0.2 pct C-1.5 pct Si-5 pct Mn transformation-induced plasticity-aided sheet steel with annealed martensite matrix were investigated for automotive applications. Both formabilities were enhanced by warm forming at peak temperatures of 423 K to 573 K and 423 K to 523 K (150 °C to 300 °C and 150 °C to 250 °C), respectively. The superior warm formabilities were mainly due to the stabilization of a large amount of retained austenite by warm forming and the consequent considerably suppressed void growth at the interface between the matrix and transformed martensite, despite there being large hole punching damage for the stretch flangeability. High peak temperatures for stretch formability and flangeability were associated with apparently increased M S of the retained austenite resulting from the increased mean normal stress on stretch forming and hole expansion.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.