Abstract
AbstractThe present study investigates the origin of voids in sheet molding compounds (SMCs) sheets and their transport during the manufacturing steps. Paste mixing, impregnation, thickening, and molding have been performed with five different SMC sheets, one without fibers and the others with four different types of glass fiber bundles. The fiber surface energy and bending rigidity were quantified, together with the paste surface energy. Void content was then measured at each manufacturing step. Two main void origins in SMC sheets have been observed: (i) air entrapment during paste mixing and (ii) poor bundle impregnation. These voids may be largely removed during SMC manufacturing. The quality of impregnation and void elimination during the flow is found to depend on the bundle characteristics (rigidity and surface energy) conferred by their sizing and over sizing. POLYM. COMPOS. 27:289–298, 2006. © 2006 Society of Plastics Engineers
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.