Visualization of structural rearrangements during annealing of solvent-crazed poly(ethylene terephthalate)

Abstract

A direct microscopic procedure is used for studying structural rearrangements during the annealing of PET samples after solvent crazing. Even at room temperature, solvent-crazed PET samples experience shrinkage which is provided by processes taking place in crazes. This shrinkage is observed at temperatures up to the glass transition temperature of PET and proceeds via drawing together of crack walls. Once the glass transition temperature is attained during annealing, the spontaneous self-elongation of the polymer sample occurs. The mechanism of this phenomenon is proposed. The low-temperature shrinkage of the polymer sample is related to the entropy contraction of highly dispersed material in crazes that has a lower glass transition temperature than that of the bulk polymer. This shrinkage cannot be complete, owing to crystallization of the oriented polymer in the volume of the crazes. As a result of crystallization, the oriented and crystallized polymer in the crazes coexists with the regions of the unoriented initial PET. As the annealing temperature approaches the glass transition temperature of the bulk PET, its strain-induced crystallization takes place. As a result, the regions of the unoriented polymer between crazes are elongated along the direction of tensile drawing and the sample experiences contraction in the normal direction.