Abstract
Visible light (VL) responsive mesoporous sulfated rare earth ions (Nd3+, La3+, Y3+) incorporated TiO2@fumed SiO2 photocatalysts were prepared by sol–gel method with P123 (EO20PO70EO20) as a template. The resultant samples were characterized by X-ray diffraction (XRD), transmission electron microscope (TEM), X-ray photoelectron spectroscopy (XPS), N2 adsorption–desorption measurements (BET), UV–vis diffuse reflectance spectroscopy, photoluminescence (PL) spectra, Fourier transform infrared spectroscopy (FTIR) and thermal analyses (TG-DTA). In comparison with nondoped sample, RE-doped samples showed not only an increase in the surface areas and pore volumes, but also an inhibition of titania phase transition from anatase to rutile. Photo-degradation results revealed that RE-doped samples could greatly improve the photocatalytic activity, and the experimental degradation rates of methyl orange (MO) were higher than that catalyzed by undoped samples and Degussa P-25, obeyed the order of Nd3+>La3+>Y3+. Nd-doped sample expressed the highest photoactivity and the optimal dosage was 0.25mol%, which resulted in MO degradation rates of 99.8% and 90.05% irradiation under UV for 60min and VL (λ>400nm) for 40h, respectively. The enhanced photocatalytic activity could be attributed to the higher specific area, good crystallinity, strong VL absorption and effective separation of photogenerated electron–hole pairs in the catalyst.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.