Abstract
AbstractViscosity measurements of GaInSn eutectic alloys were performed in a homebuilt device for low (9%) and high (95%) relative humidity for shorter (450 min) and longer (1800 min) time periods. At constant exposure time a characteristic increase of viscosity is observed with increasing humidity. For high humidity, high viscosity is obtained after a short time.Assuming that the measured viscosity change is strongly related to the absorption of oxygen, XPS was applied to the chemical and quantitative analysis of differently prepared samples. In all cases, Ga is predominantly oxidized at the surface whereas Ga atoms in the metallic state are located deeper inside. Besides Ga2O3 (the most stable oxide phase), the less stable Ga2O is detected. Indium and tin are almost stable in their metallic state. With increasing humidity the thickness of the oxide film increases in our case from about 19 Å to 25 Å, assuming a layer‐by‐layer model. The presented results confirm our assumption of the increase in viscosity of the GaInSn system as a consequence of the preferential oxidation of gallium in the near‐surface region. Copyright © 2004 John Wiley & Sons, Ltd.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.