Abstract
Nanohydroxyapatite reinforced poly(vinyl alcohol) gel (nano-HA/PVA gel) composites has been proposed as an articular cartilage repair biomaterial. In this paper, nano-HA/PVA gel composites were prepared by in situ synthesis nano-HA particles in PVA solution and accompanied with freeze/thaw method. The influence of nano-HA content, PVA concentration, test frequency and freeze/thaw cycle times on the viscoelastic behavior of nano-HA/PVA gel composites were evaluated using dynamic mechanical thermal analysis (DMTA). The results showed that both storage modulus and loss modulus firstly increased and then presented decreasing trend with the rise of nano-HA content. Their maximum values were obtained while nano-HA content was 6%. Furthermore, the G' and G'' of the composites improve with the increase of PVA concentrations and freeze/thaw cycle times. This effect was more distinct at low freeze/thaw cycles. The phase angle (tan delta) of the pure PVA gel is larger than that of the nano-HA/PVA composites at the test frequency spectra, but all the phase angle values of the tested composites were close to that of nature bone.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Materials Science: Materials in Medicine
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.