Abstract
AY2Si3O10 (A = Sr, Ba) trisilicate ceramics were synthesized by traditional high temperature solid state reaction method. X-ray diffraction patterns and Rietveld refinement revealed that AY2Si3O10 (A = Sr, Ba) ceramics belonged to triclinic and monoclinic crystal systems with Pī and P21/m space groups, respectively. The vibrational modes of [SiO4] tetrahedra, [YO6] octahedra and [(Sr/Ba)O8] polyhedra were analyzed by Raman spectroscopy. The infrared spectroscopy fitting analysis was used to determine intrinsic dielectric properties. Excellent microwave dielectric properties were measured for SrY2Si3O10 and BaY2Si3O10 with ɛr = 9.3, Qf = 64100 GHz, τf = −31 ppm/°C and ɛr = 9.5, Qf = 65600 GHz, τf = −28 ppm/°C, respectively. Both trisilicate ceramics are considered potential candidates for 5G and mm wave technology, provided τf can be further tuned.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.