Abstract
AbstractHigh cycle fatigue (HCF) and very high cycle fatigue (VHCF) properties of two 18Ni maraging steels with different cobalt and titanium content and similar static strength are investigated. Ultrasonic fatigue tests are performed with thin sheets with nitrided surfaces at load ratio R = 0.1. The specimens are mounted on a carrier and are forced to joint vibrations at approximately 20 kHz. The increase of Co content and the elimination of Ti improved the HCF and VHCF strength of 18Ni maraging steel. TiN inclusions if Ti is present and Al2O3 inclusions in the Ti free material with sizes (areaINC)1/2 smaller than 10 µm were preferential crack initiation locations. Considering inclusions as initial cracks, the minimum stress intensity range for VHCF failure is 1.2 MPam1/2 for TiN inclusions and 1.8 MPam1/2 for Al2O3 inclusions. Data scatter may be slightly reduced if lifetimes are presented versus stress amplitudes multiplied by (areaINC)1/12 rather than in an S–N diagram.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Fatigue & Fracture of Engineering Materials & Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.