Abstract
In this paper, the SAE52100 bearing steel contained large quantities of cementite dispersed in ferrite matrix was subjected to the ultrasonic nanocrystalline surface modification (UNSM) treatment that aims for the extension of fatigue life. The microstructure and fatigue life of the untreated and treated specimens were studied by using electron backscattered diffraction (EBSD) and transmission electron microscopy (TEM), and a developed ultra-high cycle fatigue test (UFT). After UNSM treatment, the coarse ferrite grains (- 10 μm) were refined to nanosize (- 200 nm), therefore, nanostructured surface layers were fabricated. Meanwhile, in the deformed layer, the number density and area fraction of cementite were increased up to - 400% and - 550%, respectively, which increased with the decrease in depth from the topmost treated surface. The improvement of hardness (from 200 Hv to 280 Hv) and high cycles fatigue strength by - 10% were considered the contribution of the developed nanostructure in the UNSM treated specimen.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.