Abstract
To improve the current grinding procedure of the back-up roll of CVC hot rolling mills so that the back-up roll service life can be extended, the crack initiation and propagation behavior of medium carbon bainitic back-up roll steel was investigated, a kind of asperity-scale, surface originated vertical short cracks occurred at 5 × 102 − 1 × 104 cycles. Theoretical analysis indicated that the maximum tensile stress occurring at the back edge of the contact of asperities keeps at above 1 347.97 MPa, and ratcheting and cyclic plastic deformation take place at such sites within 1 × 104 cycles. The early initiation of the vertical short cracks is caused by the asperity contact. According to the crack initiation mechanism, short crack behavior and preventive grinding strategy, steel consumption can be reduced considerably by decreasing the surface roughness and removing the asperity influenced surface thin layer at about 70%–80% of the surface distress life.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.