Abstract
The objective of this work is to test a novel approach to increase the bulk density of ceramic parts made by vat photopolymerization. It is hypothesized that the bulk density of the resultant ceramic parts increases by introducing a small amount of fine powder to the suspension feedstock. A commercial 3D printer was used to produce samples from different suspensions. The printed samples then underwent debinding and sintering processes, after which density and porosity measurements and microstructural characterization were carried out. It could be summarily concluded that the substitution of a small volume of a coarser (0.8 µm) powder with a finer powder (0.3 µm or 0.5 µm) in the suspension markedly increased the bulk density and decreased apparent porosity of the printed and sintered parts without worsening the printability of the suspension. Scanning electron microscopy showed the fine powder improved the necking during sintering, contributing to the increased density and decreased porosity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.