Abstract
AbstractThe complex ceramic core used for hollow turbine blades requires high porosity and flexural strength. This work combined vat photopolymerization 3D printing with sacrificial template method to prepare Al2O3 ceramic cores with strip‐shaped pores using polyamide 6 (PA6) fibers as templates. When the porosity was greater than 30%, the maximum flexural strength reached up to 110.48 MPa. The sacrificial templating method improved the porosity of Al2O3 ceramic cores, forming an internal porous structure that combined strip‐shaped large pores with irregularly shaped small pores. The influences of PA6 fiber content and diameter on the shrinkage, porosity, microstructure, and comprehensive properties of alumina ceramic cores were studied, revealing the mechanism of the coexistence of high porosity and high strength.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.