Abstract
In this research, pure SnO2 and Ni-doped SnO2 (Ni:SnO2) nanocomposite films were produced by chemical bath deposition method and the latter were coated with multi-walled carbon nanotubes (Ni:SnO2/MWCNTs) or graphene nanoplatelets (Ni:SnO2/GNPs) by spin coating. All samples have tetragonal rutile SnO2 structure with the presence of carbon (002) peak in MWCNTs- or GNPs-coated films. Crystallite size of SnO2 films decreased remarkably with Ni doping followed by a slight decrease with MWCNTs coating and slight increase with GNPs coating. Scanning electron microscope images manifested a dispersed agglomerative nature of SnO2 nanoparticles which reduced especially with MWCNTs coating due to the porous surface provided by carbon nanotubes. From the photoluminescence measurements, oxygen defects-related peaks were spotted in the SnO2-based structures with different luminescence intensities. The most significant decrease in resistance was observed with the addition of GNPs into Ni-doped SnO2 nanocomposites compared to the other produced films mainly due to the synergetic effect that promotes excellent charge transfer between surfaces of Ni:SnO2 and graphene nanosheet. The huge increase in conductivity of GNPs-coated films led to a huge increase in dielectric losses and this followed by a drop down of dielectric constant of the GNPs-coated films.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.