Vapour breakthrough behaviour of carbon tetrachloride - A simulant for chemical warfare agent on ASZMT carbon: A comparative study with whetlerite carbon

Abstract

ASZMT and whetlerite carbon was prepared by impregnation of active carbon with ammonical salts of Cu (II), Ag (I), Zn (II), Mo (VI), TEDA and Cu (II), Ag (I), Cr (VI), NaOH, C5H5N respectively using incipient wetness technique. Thereafter, impregnated carbon systems were characterized using scanning electron microscopy, energy dispersive X-ray, atomic absorption spectroscopy, thermogravimetry and surface characterization techniques. Impregnated carbon systems were evaluated under dynamic conditions against carbon tetrachloride (CCl4) vapour that was used as a simulant for the persistent chemical warfare agents for testing breakthrough times of filter cartridges and canisters of gas masks in the national approval test of respirators. The protective potential of ASZMT carbon was compared with the whetlerite carbon which is presently used in NBC filtration system. The effect of CCl4 concentration, test flow rate, temperature and relative humidity on the breakthrough behaviour of the impregnated carbon systems has also been studied. The study clearly indicated that the whetlerite carbon possessed breakthrough time greater than ASZMT carbon. However, ASZMT carbon provided adequate protection against CCl4 vapours and can be used as an alternative to whetlerite carbon that contain Cr(VI), which is reported to be carcinogenic and having lesser shelf life. The study indicated the breakthrough time of impregnated carbon systems were found to decrease with the increase of the CCl4 concentration and flow rate. The variation in temperature and relative humidity did not significantly affect the breakthrough behaviour of impregnated carbon systems at high vapour concentration of CCl4 whereasbreak through time of impregnated carbon systems reduced by an increase of relative humidity at low CCl4 vapour concentration.