Abstract
The influence of the poly( d, l-lactic acid) (PDLLA) coating thickness on the in vitro vancomycin release from a hydroxyapatite (HA) carrier was studied. Microporous HA fibers with a porosity of 51 v% and an average pore diameter of 1.0 μm were fabricated by a diffusion-induced phase separation technique. They were loaded with 38 mg vancomycin hydrochloride (VH)/g HA, and their cylindrical shape enabled the application of the spray coating technique for the deposition of uniform PDLLA coating thicknesses, varying from 6.5 μm to 28 μm. The resulting in vitro VH release varied from a complete release within 14 days for 6.5 μm coatings to a release of 23% after 28 days for 28 μm coatings. It was clear that the VH release rate from a HA fiber can be adjusted by varying the PDLLA coating thickness. Microbiological tests of these fibers against a methicillin-resistant Staphylococcus aureus (MRSA) isolate pointed to the importance of the initial burst release and confirmed that the released antibiotics had the potential to interfere with S. aureus biofilm formation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: European Journal of Pharmaceutics and Biopharmaceutics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.