Abstract
Pseudocapacitive or electrochemically active materials can achieve capacitance values up to 10-100 times greater than those obtained by materials based only on an electric double layer (EDL) mechanism. The pseudocapacitive behavior of transition metal oxides has been extensively studied in the last decades and assigned to redox reactions occurring at the surface of the material. Very recently, transition metal nitrides such as MoxN, VN or TiN have emerged as promising electrode materials for electrochemical capacitors. These materials are inexpensive, have a high molar density good chemical resistance and, most importantly, in contrast to oxides they exhibit very high electronic conductivity value. Extremely high specific capacitance values of 1340 F g-1 was reported for nanostructured VN [1]. To shed some light on the mechanism of such huge capacitance we have carried out a comparative study of VN thin films and VN nanoclusters grown and characterized in-situ to relate electrochemical properties with the structure and composition of the surface of vanadium nitride. An UHV system (SPECS) equipped with tools for XPS, e-beam assisted evaporation of metals, high pressure cell and electrochemical cell for I-V cycling was used for in-situ synthesis and characterization. A recipe to grow VN thin films and nanoclusters via direct nitridation of thin vanadium film in atmosphere of 1 bar N2 at temperature 800 oC has been developped. Stoichiometry of the VNxOy compounds can be controoled by post oxidation of VN in oxygen atmosphere at elevated temperature. Growth of VN nanoclusters using the same procedure has been performed on HOPG surface. Electrochemical characterization of VN and VNxOy thin films demostrated impressive areal capacitance of ~2000 µFcm-2 in 1M KOH electrolyte at scan rate 1Vs-1. XPS characterizationwas applied to elucidate electrochemical reactions occurring on the surface of VN films. [1] D. Choi et al., Adv. Mater., 18, 1178 (2006)
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.