Abstract
The decisive aim of the present study is to enhance the transparent conducting properties of Mo + F co-doped ZnO films through annealing. In this work, Mo + F co-doped ZnO (MFZO) films were deposited on glass substrates at a deposition temperature of 350 °C using a home-made nebulizer spray pyrolysis technique and the prepared samples were annealed under air and vacuum atmosphere at 400 °C for 2 h. The structural, electrical, optical, surface morphological and elemental properties of as-deposited, air-annealed and vacuum-annealed samples were compared using various analytical techniques. The vacuum-annealed sample shows lowest resistivity of 1.364 × 10−3 Ω cm and high transmittance of 90% in the visible region with high ohmic conducting nature. The optical bandgap of the sample was found to be increased to 3.36 eV after vacuum annealing treatment. The XRD patterns of the films confirmed the polycrystalline nature. The PL measurements show the defect levels of the deposited films. The FESEM and AFM studies show an increase in the grain size and roughness of the films, respectively, after vacuum-annealing treatment. The presence of the elements before and after annealing treatment was confirmed using XPS analysis.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.